| US$2.00-4.00 | 500 kg (MOQ) |
| GRADE | FEATURES | APPLICATION |
| GF Reinforced PBT | 10%-50% GF reinforced, high strength, low warpage. | Electric cooker, soybean milk and juice maker and other home appliances, air condition shell, car accessories, fan heater, instrument panel, thermal jug... New Energy vehicle charging pile and charging gun, automotive, MCB, appliance parts, low-temperature resistant nylon tie band, power tools, office chair base, hydrant handle, ski equipment components, breaker, connector... Battery cell jar case, heating appliances case, panel, plug, electronic shell, instrument frame, auto parts and etc... |
| Flame Retardant PBT | Fire resistant V0-5VA, high toughness, easy de-molding. | |
| High-Temperature PBT | High temperature resistant 108-115 degrees centigrade. |
| Product Description | Applications | ||||||||
| ·30%PBT 30% glass fiber reinforced PBT | · Injection molding | ||||||||
| · Excellent heat stability | · Good mechanical properties balance | ||||||||
| Properties | Test Method | Test Condition | Unit | Typical Values | |||||
| Physical properties | |||||||||
| Specific Gravity | ISO 1183 | 23ºC | g/cm3 | 1.6 | |||||
| Ash | ISO 3451 | 800ºC,30min | % | 30 | |||||
| Mechanical properties | |||||||||
| Tensile Strength | ISO 527 | 50mm/min | MPa | 130 | |||||
| Elongation at Break | ISO 527 | 50mm/min | % | 3 | |||||
| Tensile Modulus | ISO 527 | 1mm/min | MPa | 10900 | |||||
| Flexural Modulus | ISO 178 | 2mm/min | MPa | 5300 | |||||
| Charpy Notched Impact Strength | ISO 179-1eA | 23ºC | kJ/m2 | 7 | |||||
| Charpy Unotched Impact Strength | ISO 179-1eU | 23ºC | kJ/m2 | 45 | |||||
| Thermal properties | |||||||||
| Heat deflection temperature | ISO 75 | 1.80MPa | C | 185 | |||||
| Melting Point | DSC | - | C | 222 | |||||
| Other properties | |||||||||
| Flammability | UL94 | - | 1.6mmV0 | ||||||
| Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Before using the material, please consult with TOPO Co., Ltd | |||||||||