| US$3.50 | 1 kg (MOQ) |
| Liner density | Density | No. of Filament | Breaking Tenacity | Elongation at Break | Hot air Shrinkage(10 min,177ºC) | Boiling water shrinkage (30 min) | |
| Dtex | Denier | F | G/D | CN/dtex | % | % | % |
| 33 | 30 | 12 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 45 | 40 | 18 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 56 | 50 | 24 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 61 | 55 | 24 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 78 | 70 | 30 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 95 | 85 | 30 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 111 | 100 | 36 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 125 | 112 | 36 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 133 | 120 | 36 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 140 | 126 | 48 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 167 | 150 | 48 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 233 | 210 | 72 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 278 | 250 | 72 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 333 | 200 | 96 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
| 467 | 420 | 144 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |