| US$10.00-50.00 | 5 kg (MOQ) |
| Material | tungsten carbide |
| Chemical Composition | WC≥ 85.0% |
| Hardness (HV) | 1475~1675 |
| Hardness (HRC) | 45/50/55/58/60/65 |
| Compressive Strength (N/mm2) | 5600 |
| Transverse-rupture strength (N/mm2) | 3600 |
| Frature Toughness | 10 |
| Grade | ISO | Density (g/cm3) | Hardness(HRA) | T.R.S.(N/mm2) | Application |
| YT5 | P30 | 12.9 | 90.5 | 2200 | Best strength, high impact and shock resistance among W-Co-Ti alloys, but comparatively lower wear resistance. Suitable for rough turning, rough planning, and semi-finish planning of carbon steel, and alloy steel including forgings, stamped parts, and cast iron surfaces during intermittent cutting. |
| YW1 | M10 | 13 | 92.5 | 1710 | Better hardness, resistant to impact load. A good grade for general purposes. Suitable for machining of ordinary steel, cast irons as well as steels hard to be machined such as refractory steel, high manganese steel, and stainless steel, etc |
| YW2 | M20 | 12.9 | 91 | 1880 | Higher wear resistance and strength, resistant to high impact load. Suitable for roughing and semi-finishing of ordinary steel, and cast irons as well as refractory steel, high manganese steel, and high-grade alloy steel, etc |
| YG6X | K10 | 14.8 | 91.5 | 1890 | Fine grain WC alloy, wear resistance higher than YG6, strength close to YG6. Suitable for machining chilled alloy cast irons, and refractory alloy steel, as well as finishing of ordinary cast irons |
| YG6 | K20 | 14.8 | 89.5 | 2050 | High wear resistance, better impact and shock resistance. Suitable for semi-finishing, and finishing of cast irons, non-ferrous metal, alloys, and non-metallic materials at moderate cutting speed |
| YG8 | K30 | 14.6 | 89 | 2520 | High strength, better impact and shock resistance, but lower wear resistance and cutting speed. Suitable for roughing of cast irons, non-ferrous metal, alloys, and non-metallic materials at low speed. |
| YT15 | P10 | 11.3 | 92 | 1650 | Higher wear resistance with a certain impact toughness, Suitable for semi-finishing of medium chip sections, or finishing of small chip sections of steel, cast steel, alloy steel. |