Wholesale Best Seller N06200/2.4675/ASTM B574/ASTM B575/ASTM B619 Super Alloy Plate for Oil Processing Hastelloy C2000 Sheet

Product Description

Product Description
Introduction HASTELLOY C-2000 alloy (UNS N06200) is unique among the versatile nickel-chromium-molybdenum materials in having a deliberate copper addition. This provides greatly enhanced resistance to sulfuric acid. It also has a high chromium content, to maximize its resistance to oxidizing chemicals and process streams contaminated with ferric ions and dissolved oxygen.
Like other nickel alloys, it is ductile, easy to form and weld, and possesses exceptional resistance to stress corrosion cracking in chloride-bearing solutions (a form of degradation to which the austenitic stainless steels are prone). It is able to withstand a wide range of oxidizing and non-oxidizing chemicals, and exhibits outstanding resistance to pitting and crevice attack in the presence of chlorides and other halides.
HASTELLOY C-2000 alloy is available in the form of plates, sheets, strips, billets, bars, wires, pipes, tubes, and covered electrodes. Typical chemical process industry (CPI) applications include reactors and heat exchangers.
Composition
The chemical composition of stainless steel grade Hastelloy C-2000 is outlined in the following table.

Element	Min %	Max %
Cr	22.00	24.00
Mo	15.00	17.00
Fe	-	3.00
C	-	0.01
Si	-	0.08
Co	-	2.00
Mn	-	0.50
P	-	0.025
S	-	0.01
Cu	1.30	1.90
Al	-	0.50
Ni	bal

Grade Specification

Grade	UNS	DIN	EN	AMS	ASTM		JIS
Hastelloy C-2000	N06200		2.4675		ASTM B574 ASTM B575 ASTM B619		-

Welding and Fabrication HASTELLOY C-2000 alloy is very amenable to the Gas Metal Arc (GMA/MIG), Gas Tungsten Arc (GTA/TIG), and Shielded Metal Arc (SMA/Stick) welding processes.
Wrought products of HASTELLOY C-2000 alloy are supplied in the Mill Annealed (MA) condition, unless otherwise specified. This solution annealing procedure has been designed to optimize the alloy's corrosion resistance and ductility. Following all hot forming operations, the material should be re-annealed, to restore optimum properties. The alloy should also be re-annealed after any cold forming operations that result in an outer fiber elongation of 7% or more. The annealing temperature for HASTELLOY C-2000 alloy is 1149°C (2100°F), and water quenching is advised (rapid air cooling is feasible with structures thinner than 10 mm (0.375 in). A hold time at the annealing temperature of 10 to 30 minutes is recommended, depending on the thickness of the structure (thicker structures need the full 30 minutes).
HASTELLOY C-2000 alloy can be hot forged, hot rolled, hot upset, hot extruded, and hot formed. However, it is more sensitive to strain and strain rates than the austenitic stainless steels, and the hot working temperature range is quite narrow. For example, the recommended start temperature for hot forging is 1232°C (2250°F) and the recommended finish temperature is 954°C (1750°F). Moderate reductions and frequent re-heating provide the best results, as described here. This reference also provides guidelines for cold forming, spinning, drop hammering, punching, and shearing. The alloy is stiffer than most austenitic stainless steels, and more energy is required during cold forming. Also, HASTELLOY C-2000 alloy work hardens more readily than most austenitic stainless steels, and may require several stages of cold work, with intermediate anneals.
While cold work does not usually affect the resistance of HASTELLOY C-2000 alloy to general corrosion, and to chloride-induced pitting and crevice attack, it can affect resistance to stress corrosion cracking. For optimum corrosion performance, therefore, the re-annealing of cold worked parts (following an outer fiber elongation of 7% or more) is important.
Physical Properties
The physical properties of Hastelloy(r) C-2000(r) are highlighted in the following table.

Properties	Metric	Imperial
Density	8.50 g/cm³	0.307 lb/in³

Mechanical Properties
The mechanical properties of Hastelloy(r) C-2000(r) flat products are given in the following table.

Properties	Metric	Imperial
Tensile strength (@ thickness 25.4 mm/ 1.00 in.)	752 MPa	109000 psi
Yield strength (@ 20°C/ 68°F, thickness 12.7 mm/0.5000 in, 0.2% offset)	345 MPa	50000 psi
Elongation at break (@ thickness 6.35 mm/0.250 in., in 50.8 mm)	62%	62%

Hastelloy C-2000 Standards

Seamless Pipe & Tube	Welded Pipe & Tube	Fittings	Billet, Rod and Bar	Forgings	Plate, Sheet and Strip
ASTM B622	ASTM B619 ASTM B626	ASTM B366 ASTM B462	ASTM B574	ASTM B564 ASTM B462	ASTM B575

Applications Flare tips Fluidized bed coal combustors Radiant tubes Tube hangers for petroleum refining and steam boilers Coal gasifier internal components Thermowells and refractory anchor bolts Burners, combustion chambers Retorts, muffles, annealing covers Cryogenic structures Surface Treatment

Processing
Packaging & Shipping
Company Profile
FAQ

---

>> Luxury Backwash Head SPA Hair Wash Salon Shampoo Chair Bed
>> Wholesale 300ml Craft Beer Glass Long Stem Goblet Glass with Customized Logo
>> 001*7 Strong Acid Cation Resin beads ion exchange resin
>> CE Approved Homogenizer Blender with Clamp Connection
>> Best 50cc Gasoline Moped Motorcycle Africa Mini Fuel Efficient Small Motorbike Loading Motorcycle Chopper Motorcycles for Sale Gasoline Engine Motorcycle
>> Vmc850 Vmc855 Vmc1160 High Accuracy Metal Processing Vertical Machining Center
>> BOPP jumbo roll
>> Toughened fast-curing epoxy adhesive
>> TMAXCN High Quality Double Doctor Blade Micrometer Film Applicator with 150mm Width
>> Her101--Her108 1A 1000V Discrete Semiconductors Diodes Rectifiers Fast Recovery Rectifiers Do-41
>> Module spare parts ABBTP830
>> Lower Price 18L Dental Autoclave with The Digital Display
>> Hybrid CNC Bending Machine CNC Press Brake for Metal Steel/ Ss/ CS
>> Hot Sell Self-Walking Tmr Feed Mixer Cattle Equipment Machine
>> Automatic Baklava Pillow Pouch Packaging Machine Plastic,wood Packaging Center / Back Sealing Max.320mm 50~150mm Max.70mm PLC
>> Gogo Holland Potato (50 - 100grams)
>> 1/12HP Brushless DC/Ec Condenser Fan Motor for Outdoor Air Conditioning Coil Units and Air Cooler
>> portable road coring machine using in road asphalt testing
>> Family Use Electric Mill Making 7.5kw Mini 2mm Model 160 Low Cost Poultry and Livestock Feed Pellet Machine
>> OEM High Precision Bracket Stainless Steel Sheet Metal Stamping Parts for Wheelbarrow