| US$950.00-1,020.00 | 20 Tons (MOQ) |
HDPE cable material Property | Unit | Typical Value |
Mass density | g/cm³ | 0.941-0.959 |
Melt flow Rate(190 Centigrade /2.16kg) | g/10min | ≤1.0 |
Tensile yield strength | MPa | ≥19.0 |
Flexural modulus | Mpa | ≥965 |
Elongation@ break | % | ≥400 |
Impact Embrittlement temperature | Centigrade | MAX -118 |
Dielectric Constant | 100KHZ | 2.32 |
1MHZ | 2.31 | |
Loss Tangent | 100KHZ | MAX 0.0001 |
1MHZ | MAX 0.0001 | |
Volume resistivity | OHM-CM | MIN 1x10 15 |
| Item | Test method | Test data | Data unit |
| MFR(190ºC,2.16KG) | ASTM D1238 | 0.3 | g/10min |
| Density | ASTM D792 | 0.956 | g/cm³ |
| Tensile yield strength | ASTM D638 | 25 | Mpa |
| Tensile breaking strength | ASTM D638 | 38 | Mpa |
| flexural modulus (2% secant) | ASTM D790 | 860 | Mpa |
| Elongation at break | ASTM D638 | 950 | % |
| Environmental stress cracking resistance (50°C, 100% Igepal, F50) | ASTM D1693 | >200 | hr |
| Vicat softening point | ASTM D1525 | 128 | ºC |
| Notched impact strength of cantilevered beams(23ºC) | ASTM D256 | 130 | J/m |
| Shore hardness(D) | ASTM D2240 | 66 |