1. Product description
5. Shipping & package : customized package is accepted
1. Paint is Pour into bucket and cover the bucket tight;
2. Buckets are put one by one closely with rope to bind together tightly
3. Wrapped by shrink film 3 times with pallets under;
4. Loaded by FCL/ LCL container;
7. Product Data
| Polyaspartic Garage Floor Top Coating Data Sheet |
| Product Name | Polyaspartic Garage Floor Coating- Type A (T23090189) |
| Main Raw Material | Polyaspartic polyurea resin |
| No# | Project | Data |
| 1 | Drying time | surface dry | 2H, can be walked by people |
| full dry | 3 days ,Also affected by local temperature |
| 2 | Tensile strength (500±50) mm/min,MPa | 21.89 |
| 3 | Elongation at break (500±50) mm/min,% | 525 |
| 4 | Tearing strength (500±50) mm/min,N/mm | 78 |
| 5 | Bending at low temperature | -35ºC, no cracks |
| 6 | Impermeability | 0.3MPa,120min, No permeability |
| 7 | Water absorption rate % | 1.9 |
| 8 | Bond strength (Under standard experimental conditions, MPa) | 3.20 (Substrate Failure ) |
| 9 | Acid treatment (2% H2SO4 solution 7d) | Tensile strength retention rate % | 77 |
| Elongation at break % | 632 |
| Bending at low temperature | -30ºC,no cracks |
| 10 | Alkaline treatment 0.1% NaOH solution +saturated Ca(OH)2 solution ,7d | Tensile strength retention rate % | 78 |
| Elongation at break % | 598 |
| Bending at low temperature | -30ºC,no cracks |
| 11 | Salt treatment (3%NaCI solution ,7d) | Tensile strength retention rate % | 79 |
| Elongation at break % | 603 |
| Bending at low temperature | -30ºC,no cracks |
| 12 | Artificial climate aging (2745h) | Apperance | No cracks |
| Tensile strength retention rate % | 92 |
| Elongation at break % | 567 |
| Bending at low temperature | -30ºC,no cracks |
| 13 | Water resistance (indoor temperature 14d ) | No cracks, no layering, no sticking, no foaming, no breakage |
| 14 | Wear resistance (750g/500r) ,mg | 14 |
| 15 | Impact resistance,1.0kg.m | No damage |
| Shanghai Juneso New Materials Co.,Ltd |